Electrode including silicon-comprising fibres and electrochemical cells including the same

ABSTRACT

A pre-charged material including silicon-comprising fibers characterized in that two or more of the fibers are bonded together to create both a bonded felt anode structure, with or without a current collector, and a composite anode structure with a current collector and an electrode structure. The structure overcomes problems associated with charge/discharge capacity loss.

The invention relates to a method of fabricating bonded fibres composed of silicon or a silicon-based material and their use as the active anode material in rechargeable lithium battery cells.

The recent increase in the use of portable electronic devices such as mobile telephones and note book computers and the emerging trend of using rechargeable batteries in hybrid electric vehicles has created a need for smaller, lighter, longer lasting rechargeable batteries to provide the power to the above mentioned and other battery powered devices. During the 1990s, lithium rechargeable batteries, specifically lithium ion batteries, became popular and, in terms of units sold, now dominate the portable electronic marketplace and are set to be applied to new, cost sensitive applications. However, as more and more power hungry functions are added to the above mentioned devices, (e.g. cameras on mobile phones), improved and lower cost batteries that store more energy per unit mass and per unit volume are required.

It is well known that silicon can be used as the active anode material of a rechargeable lithium-ion electrochemical cell (see, for example, Insertion Electrode Materials for Rechargeable Lithium Batteries, M. Winter, J. O. Besenhard, M. E. Spahr, and P. Novak in Adv. Mater. 1998, 10, No. 10). The basic composition of a conventional lithium-ion rechargeable battery cell is shown in FIG. 1 including a graphite-based anode electrode, the component to be replaced by the silicon-based anode. The battery cell includes a single cell but may also include more than one cell.

The battery cell generally comprises a copper current collector for the anode 10 and an aluminium current collector for the cathode 12 which are externally connectable to a load or to a recharging source as appropriate. A graphite-based composite anode layer 14 overlays the current collector 10 and a lithium containing metal oxide-based composite cathode layer 16 overlays the current collector 12. A porous plastic spacer or separator 20 is provided between the graphite-based composite anode layer 14 and the lithium containing metal oxide-based composite cathode layer 16 and a liquid electrolyte material is dispersed within the porous plastic spacer or separator 20, the composite anode layer 14 and the composite cathode layer 16. In some cases, the porous plastic spacer or separator 20 may be replaced by a polymer electrolyte material and in such cases the polymer electrolyte material is present within both the composite anode layer 14 and the composite cathode layer 16.

When the battery cell is fully charged, lithium has been transported from the lithium containing metal oxide via the electrolyte into the graphite-based layer where it reacts with the graphite to create the compound, LiC₆. The graphite, being the electrochemically active material in the composite anode layer, has a maximum capacity of 372 mAh/g. It will be noted that the terms “anode” and “cathode” are used in the sense that the battery is placed across a load.

It is generally believed that silicon, when used as an active anode material in a lithium-ion rechargeable cell, provides a significantly higher capacity than the currently used graphite. Silicon when converted to the compound Li₂₁Si₅ by reaction with lithium in an electrochemical cell, has a capacity of 4,200 mAh/g.

Existing approaches of using a silicon or silicon-based active anode material in a lithium-ion electrochemical cell have failed to show sustained capacity over the required number of charge/discharge cycles and are thus not commercially viable.

One approach uses silicon in the form of a powder, in some instances made into a composite with optionally an electronic additive and containing an appropriate binder such as polyvinylidene difluoride coated onto a copper current collector. However, this electrode fails to show sustained capacity when subjected to charge/discharge cycles. It is believed that this capacity loss is due to partial mechanical isolation of the silicon powder mass arising from the volumetric expansion/contraction associated with lithium insertion/extraction into and from the host silicon. In turn, this give rise to electrical isolation of the silicon elements from both the copper current collector and themselves. In addition, the volumetric expansion/contraction causes the spherical elements to be broken up causing a loss of electrical contact within the spherical element itself.

Another approach known in the art, designed to deal with the problem of the large volume changes during successive cycles is to make the size of the silicon elements that make up the silicon powder very small, that is to use spherical particles that have diameters in the 1-10 nm range. This strategy assumes that the nano-sized elements can undergo the large volumetric expansion/contraction associated with lithium insertion/extraction without being broken up or destroyed. However, the approach is problematic in that it requires the handling of very fine, nano-sized powder that may pose a healthy and safety risk and it does not prevent the electrical isolation of the spherical elements from both the copper current collector and themselves as the silicon powder undergoes the volumetric expansion/contraction associated nano-sized elements can give rise to the creation of a lithium-containing surface film that introduces a large irreversible capacity into the lithium-ion battery cell. In addition, the large number of small silicon particles creates a large number of particle-to-particle contacts for a given mass of silicon and these each have a contact resistance and may thus cause the electrical resistance of the silicon mass to be too high. The above problems have thus prevented silicon particles from becoming a commercially viable replacement for graphite in lithium rechargeable batteries and specifically lithium-ion batteries.

In another approach described by Ohara et al. in Journal of Power Sources 136 (2004) 303-306 silicon is evaporated onto a nickel foil current collector as a thin film and this structure is then used to form the anode of a lithium-ion cell. However, although this approach gives good capacity retention, this is only the case for very thin films (say ˜50 nm) and thus these electrode structures do not give usable amounts of capacity per unit area. Increasing the film thickness (say >250 nm) causes the good capacity retention to be eliminated. The good capacity retention of these thin films is considered by the present inventors to be due to the ability of the thin film to absorb the volumetric expansion/contraction associated with lithium insertion/extraction from the host silicon without the film being broken up or destroyed. Also, the thin film has a much lower surface area than the equivalent mass of nano-sized particles and thus the amount of irreversible capacity due to the formation of a lithium-containing surface film is reduced. The above problems have thus prevented a thin film of silicon on a metal foil current collector from becoming a commercially viable replacement for graphite in lithium rechargeable batteries and specifically lithium-ion-batteries.

In another approach described in U.S. 2004/0126659, silicon is evaporated onto nickel fibres which are then used to form the anode of a lithium battery. However this is found to provide an uneven distribution of silicon on the nickel fibres hence significantly affecting operation. In addition, these structures have a high ratio of nickel current collector mass to active silicon mass and thus do not give usable amounts of capacity per unit area or per unit mass.

In another approach described in U.S. Pat. No. 6,887,511, silicon is evaporated onto a roughened copper substrate to create medium-thickness films of up to 10 μm. During the initial lithium ion insertion process, the silicon film breaks up to form pillars of silicon. These pillars can then reversibly react with lithium ions and good capacity retention is achieved. However, the process does not function well with thicker film and the creation of the medium-thickness film is an expensive process. Furthermore the pillared structure caused by the break up of the film has no inherent porosity such that issues may arise with long term capacity retention.

A review of nano- and bulk-silicon based insertion anodes for lithium-ion secondary cells has been provided by Kasavajjula et al (J. Power Sources (2006), doi:10,1016/jpowsour.2006.09.84) herewith incorporated by reference herein.

Another approach described in UK Patent Application GB2395059A uses an integrated silicon electrode comprising a regular or irregular array of silicon pillars fabricated on a silicon substrate. These structured silicon electrodes show good capacity retention when subjected to repeated charge/discharge cycles and this good capacity retention is considered by the present inventors to be due to the ability of the silicon pillars to absorb the volumetric expansion/contraction associated with lithium insertion/extraction from the host silicon without the pillars being broken up or destroyed.

In a further approach, PCT/GB2007/000211 with common assignees and entitled “A method of fabricating fibres composed of silicon or a silicon-based material and their use in lithium rechargeable batteries”, incorporated herewith by reference, describes a method of creating pillars of silicon on a substrate and harvesting these pillars to create silicon fibres. These fibres are then used to fabricate a composite electrode (e.g. by replacing the graphite powder in a typical graphite-based composite anode with silicon fibres) or used to fabricate a felt or felt-like structure on a current collector.

The first aspect of the invention relates to a pre-charged material comprising silicon-comprising fibres characterised in that two or more of the fibres are bonded together. For the purposes of this invention, fibres may be bonded directly to each other or may be bonded via a metal bridging element, wherein the metal bridging element is preferably one or more selected from copper, nickel, aluminium, iron, iridium, gold, titanium, lead, bismuth, antimony and silver.

For the purposes of this invention, substantially all of the fibres of the material can be bonded together. In particular, 50% or more of the fibres can be bonded together, preferably 75% or more of the fibres can be bonded together, more preferably 90% or more of the fibres can be bonded together. The material of the first aspect can therefore be provided as a bonded felt. The bonded material can give a mechanically stable structure that can withstand the mechanical handling associated with cell assembly and preserves the initial electrode structure after the cell has undergone repeated charge/discharge cycling.

Typically the fibres will have a length to diameter ratio of approximately 100:1 and hence in an anode layer such as a felt anode layer, each fibre will contact other fibres many times along their length giving rise to a configuration where the chance of mechanical isolation arising from broken silicon contacts is negligible. Bonding between the silicon comprising fibres can therefore occur at each contact point along the length of the fibre. Each fibre can therefore have one or more bonding points along its length. The insertion and removal of lithium into the fibres, although causing volume expansion and volume contraction, does not cause the fibres to be destroyed and hence the intra-fibre electronic conductivity is preserved and this feature enhances the performance of the electrode over many discharge/charge cycles.

The fibres of the invention may have transverse dimensions (i.e. width and/or depth) in the range 0.08 to 0.5 microns, preferably 0.2 microns and a length in the range 20 to 300 microns preferably 100 microns. The fibres may have an aspect ratio of about 100:1. The fibres may have a substantially circular cross-section or a substantially non-circular cross-section. The material of the first aspect can have a percentage pore volume of about 10-30 percent.

The material of the first aspect of the invention is provided for the formation of an electrode. The material of the first aspect is therefore described as pre-charged as it has not yet been incorporated into a battery and/or undergone a recharging cycle. Bonding of the two or more fibres is not therefore a result of a recharging cycle. It will be appreciated that the material of the invention can be incorporated into an electrode and ultimately into a battery, where it can undergo one or more recharging cycles.

The second aspect of the invention relates to a method of fabricating pre-charged bonded silicon-comprising fibres comprising bonding two or more of the fibres together. The fibres can be obtained by etching a substrate (such as a chip or a wafer) comprising silicon to make pillars and then detaching the pillars from the substrate to create fibres. It will be appreciated that any substrate which will allow the production of pillars can be used for the present invention. The method of the second aspect therefore comprises the steps of etching a substrate (such as a chip or a wafer) comprising silicon to make pillars, detaching the pillars from the substrate to create fibres and bonding two or more of the fibres together.

The two or more fibres can be bonded via excess pressure and/or elevated temperature. The two or more fibres can be bonded via a metal bridging element, in particular via one or more metal bridging element selected from copper, nickel, aluminium, iron, iridium, gold, titanium, lead, bismuth, antimony and silver. The two or more silicon fibres can form a compound with the metal bridging element or the metal bridging element can be electrolessly plated onto a first silicon comprising fibre and a compound formed between the metal bridging element on the first silicon comprising fibre and a second silicon comprising fibre. The metal bridging element should be capable of forming a compound with the silicon comprising fibres. The formed compound should have a high electrical conductivity. It will be appreciated that several methods exist for the addition of the metal bridging element such as the dispersion of a small particle size powder, electroless disposition onto the fibres or vapour deposition onto the fibres.

Where the two or more fibres are bonded via a metal bridging element, the fibres and metal bridging element can be heated to or above the temperature required to form an alloy between the metal bridging element and the silicon fibres.

The fibres of the present invention can be created by reactive ion etching, chemical reaction etching or galvanic exchange etching of a substrate and detached by one or more of scraping, agitating or chemical etching.

The silicon-comprising material comprises undoped silicon, doped silicon or a silicon germanium mixture. The fibre can be single crystal silicon or single crystal silicon germanium.

The third aspect of the invention provides a method of creating a cell electrode comprising depositing a slurry containing the material as described in the first aspect of the invention to form a layer of bonded silicon-comprising fibres, in particular, single crystal fibres. The method includes depositing the bonded fibres on a current collector. In particular, the third aspect of the invention provides a method of creating an anode.

In a preferred feature of the third aspect, the cell electrode can be created by depositing a slurry of fibres to form a layer of unbonded silicon-comprising fibres and then bonding two or more of the fibres together. The two or more fibres can be bonded together using any of the methods set out in the second aspect of the invention. In particular, the slurry of fibres can be deposited on a current collector, and two or more of the fibres can be bonded together using excess pressure and/or elevated temperature or by the addition of metal bridging element.

The fourth aspect of the invention provides a method of fabricating a lithium rechargeable cell comprising the steps of creating an anode as described in the third aspect of the invention and adding a cathode and an electrolyte. The method further comprises adding a separator between cathode and the anode. The method further comprises providing a casing around the cell.

The fifth aspect of the invention provides a composite electrode containing bonded silicon-comprising fibres fabricated according to the second aspect of the invention as one of its active materials. The composite of the fifth aspect of the invention uses copper as a current collector. In particular, the fifth aspect of the invention relates to a composite electrode in which the electrode is an anode.

The sixth aspect of the invention provides an electrochemical cell containing an anode as described in the fifth aspect of the invention. In particular, an electrochemical cell is provided in which the cathode comprises a lithium-containing compound capable of releasing and reabsorbing lithium ions as its active material. In particular, the sixth aspect provides an electrochemical cell in which the cathode comprises lithium-based metal oxide or phosphate as its active material preferably LiCoO₂ or LiMn_(x)Ni_(x)Co_(1-2x)O₂ or LiFePO₄.

The seventh aspect of the invention provides a lithium rechargeable cell anode comprising a bonded layer of silicon-comprising single crystal fibres. In particular, the bonded fibres are part of a composite.

There is further provided a cell comprising an anode as described above and a cathode, wherein the cathode can comprise lithium-based material, in particular, lithium cobalt dioxide.

There is further provided a device powered by a cell as described above.

Because the anode electrode structure uses fibres comprising silicon, the problems of reversibly reacting these fibres with lithium are overcome. In particular by arranging the fibres in a bonded felt structure, that is a mixture of fibres a polymer binder and an electronic additive, the charge/discharge process becomes reversible and repeatable and good capacity retention is achieved.

The fibres may be deposited as a felt or felt-like structure, wherein two or more of the fibres are subsequently bonded together via a metal bridging element to create a bonded felt or felt-like structure.

In overview the invention allows creation of bonded fibres of silicon or silicon-based material and the use of these bonded fibres to create both a bonded felt anode structure with or without a current collector and a composite anode structure with a current collector and an electrode structure. It is believed that the structure of the silicon comprising elements that make up the composite overcomes the problem of charge/discharge capacity loss

In particular, by laying down the fibres in a composite or felt or a felt-like structure, that is a plurality of elongate or long thin fibres which crossover to provide multiple intersections, for example by being laid down in a random or disordered or indeed ordered manner, the problem of charge/discharge capacity loss is reduced. The bonding of these fibres together further allow the integrity of the felt to be maintained when the bonded fibres are incorporated into an electrode and prevent problems associated with the loss of the loose fibres during manufacturing processes.

The insertion and removal of lithium into the fibres, although causing volume expansion and volume contraction, does not cause the fibres to be destroyed and hence the intra-fibre electronic conductivity is preserved.

The fibres may be manufactured by detaching pillars from a substrate, such as a silicon wafer. In addition the manner of fabrication of the pillars may be provided by a simple repeatable chemical process.

One manner in which the pillars can be made is by dry etching, for example deep reactive ion etching of the type, for example, described in U.S. application Ser. No. 10/049,736 which is commonly assigned herewith and incorporated herein by reference. The skilled person will be familiar with the process such that detailed description is not required here. Briefly, however, a silicon substrate coated in native oxide is etched and washed so as to give a hydrophilic surface. Caesium chloride (CsCl) is evaporated on the surface and the coated substrate is transferred under dry conditions to a chamber of fixed water vapour pressure. A thin film of CsCl develops into an island array of hemispheres whose dimensional characteristics depend on initial thickness, water vapour pressure and time of development. The island array provides an effective mask after which etching is carried out for example by reactive ion etching leaving an array of pillars corresponding to the hemispherical islands. The CsCl resist layer is highly soluble in water and can be readily washed away.

Alternatively the pillars can be made by wet etching/using a chemical galvanic exchange method for example as described in our co-pending application GB 0601318.9 with common assignees and entitled “Method of etching a silicon-based material”, incorporated herewith by reference. A related method which may also be used has been disclosed in Peng K-Q, Yan, Y-J Gao, S-P, Zhu J., Adv. Materials, 14 (2004), 1164-1167 (“Peng”); K. Peng et al, Angew. Chem. Int. Ed., 44 2737-2742; and K. Peng et al., Adv. Funct. Mater., 16 (2006), 387-394.

In the preferred embodiment pillars of for example 100 microns in length and 0.2 microns in diameter are fabricated on and from a silicon substrate. More generally pillars of length in the range of 20 to 300 microns and diameter or largest transverse dimension in the range of 0.08 to 0.5 microns may be used to provide the fibres. According to the process the silicon substrate may be n- or p-type and, according to the chemical approach, and may be etched on any exposed (100) or (110) crystal face. Since the etching proceeds along crystal planes, the resulting fibres are single crystals. Because of this structural feature, the fibres will be substantially straight facilitating length to diameter ratio of approximately 100:1 and, when in a composite anode layer, allowing each fibre to contact other fibres many times along their length. The etching process can also be carried out either on very large scale integration (VLSI) electronic grade wafers or rejected samples of the same (single crystal wafers). As a cheaper alternative, photovoltaic grade polycrystalline material, as used for solar panels, may also be used.

In order to detach the pillars to obtain the fibres, the substrate, with pillars attached, is placed in a beaker or any appropriate container, covered in an inert liquid such as ethanol and subjected to ultra-sonic agitation. It is found that within several minutes the liquid is seen to be turbid and it can be seen by electron microscope examination that at this stage the pillars have been removed from their silicon base.

It will be appreciated that alternative methods for “harvesting” the pillars include scraping the substrate surface to detach them or detaching them chemically. One chemical approach appropriate to n-type silicon material comprises etching the substrate in an HF solution in the presence of backside illumination of the silicon wafer.

Once the silicon comprising pillars have been detached they can be used as the active material in a composite anode for lithium-ion electrochemical cells. To fabricate a composite anode, the harvested silicon is filtered from solution and can be mixed with polyvinylidene difluoride and made into a slurry with a casting solvent such as n-methyl pyrrolidinone. This slurry can then be applied or coated onto a metal plate or metal foil or other conducting substrate for example physically with a blade or in any other appropriate manner to yield a coated film of the required thickness and the casting solvent is then evaporated from this film using an appropriate drying system which may employ elevated temperatures in the range of 50 degrees C. to 140 degrees C. to leave the composite film free or substantially from casting solvent. The resulting mat or composite film has a porous and/or felt-like structure in which the mass of silicon fibres is typically between 70 percent and 95 percent. The composite film will have a percentage pore volume of 10-30 percent, preferably about 20 percent.

Alternatively a felt or felt-like structure may be produced as a sheet material (not necessarily on a current collector) and act as its own current collector.

Fabrication of the lithium-ion battery cell thereafter can be carried out in any appropriate manner for example following the general structure shown in FIG. 1 but with a silicon comprising active anode material rather than a graphite active anode material. For example the silicon fibres-based composite anode layer is covered by the porous spacer 18, the electrolyte added to the final structure saturating all the available pore volume. The electrolyte addition is done after placing the electrodes in an appropriate casing and may include vacuum filling of the anode to ensure the pore volume is filled with the liquid electrolyte.

The manner in which the bonding of the fibres is achieved according to the present invention is illustrated with reference to one or more of the following non-limiting examples:

EXAMPLES

The fibres of the present application are produced by the production of pillars on a silicon-comprising substrate. Said pillars can be fabricated by dry etching, for example deep reactive ion etching of the type, for example, described in U.S. application Ser. No. 10/049,736 which is commonly assigned herewith and incorporated herein by reference. Alternatively the pillars can be made by wet etching/using a chemical galvanic exchange method for example as described in our co-pending application GB 0601318.9 with common assignees and entitled “Method of etching a silicon-based material”, incorporated herewith by reference. A related method which may also be used has been disclosed in Peng K-Q, Yan, Y-J Gao, S-P, Zhu J., Adv. Materials, 14 (2004), 1164-1167 (“Peng”); K. Peng et al, Angew. Chem. Int. Ed., 44 2737-2742; and K. Peng et al., Adv. Funct. Mater., 16 (2006), 387-394.

The fibres can be removed from the substrate by agitation in an ultrasonic bath. The resulting fibres are suspended in water and filtered using different various filter paper sizes to collect different size silicon fibres.

Silicon fibres obtained as set out above are mixed with copper powder and heated using an excess pressure to form a net-like structure.

Alternatively, copper is electrolessly plated onto the silicon fibres via a Galvanic exchange mechanism as described by Kim et al, Journal of Power Sources, 147 (2005) 227-233.

Alternatively, the silicon fibres are bonded together using high pressure (as set out in: Cold compaction of silicon powders without a binding agent, MATERIALS LETTERS 61 (2): 485-487 January 2007 and/or elevated temperature.

The bonded felt electrode is lightly rolled, and then electrode disks are cut out with a diameter of 12 mm. These are assembled into electrochemical cells in an argon filled glove box. The counter electrode and reference electrode are both lithium metal. The electrolyte is LiPF₆ in a mixture of organic carbonates. The cell is tested on a VMP3 device. After a thirty minute soak, the cell is held at −0.1 mA for one hour, and then at −0.2 mA until the required lithiation capacity is achieved. The electrode is then delithiated at +0.2 mA, up to a voltage of 1.0 V vs. Li/Li⁺.

A particular advantage of the approach described herein is that large sheets of silicon-comprising anode can be fabricated, rolled if necessary, and then slit or stamped out subsequently as is currently the case in graphite-based anodes for lithium-ion battery cells meaning that the approach described herein can be retrofitted with the existing manufacturing capability.

A further advantage of the arrangement described herein is that the structural strength of the in situ anode electrode in fact increases with each recharging operation. This is because the fibres are bonded to one another, at the fibre junctions, creating an amorphous structure. This in turn reduces the risk of capacity loss over multiple cycles as there is less risk of mechanical isolation of the fibres as the fibres are connected in the manner described above.

It will be appreciated, of course, that any appropriate approach can be adopted in order to arrive at the approaches and apparatus described above. For example the pillar detaching operation can comprise any of a shaking, scraping, chemical or other operation as long as pillars are removed from the substrate to create fibres. Reference to silicon-based material includes silicon where appropriate. The fibres can have any appropriate dimension and can for example be pure silicon or doped silicon or other silicon-based material such as a silicon-germanium mixture or any other appropriate mixture. The substrate from which pillars are created may be n- or p-type, ranging from 100 to 0.001 Ohm cm, or it may be a suitable alloy of silicon, for example Si_(x)Ge_(1-x). The fibres can be used for any appropriate purpose such as fabrication of electrodes generally including cathodes. The cathode material can be of any appropriate material, typically a lithium-based metal oxide or phosphate material such as LiCoO₂, LiMn_(x)Ni_(x)Co_(1-2x)O₂ or LiFePO₄. The features of different embodiments can be interchanged or juxtaposed as appropriate and the method steps performed in any appropriate order. 

The invention claimed is:
 1. An electrode comprising silicon-comprising fibres, wherein the silicon-comprising fibres are arranged to cross over each other to provide multiple intersection points, and characterized in that two or more of the fibres are bonded to each other at intersection points to form a bonded felt before any lithiation or delithiation of the silicon comprising fibres, and wherein the two or more fibres are made of the same material and have substantially the same dimensions.
 2. The electrode as claimed in claim 1 wherein substantially all of the fibres are bonded together.
 3. The electrode as claimed in claim 1 in which the fibres have transverse dimensions in the range 0.08 to 0.5 microns and a length in the range 20 to 300 microns.
 4. The electrode as claimed in claim 1 in which the fibres have an aspect ratio of about 100:1.
 5. The electrode as claimed in claim 1 in which the fibres have a substantially circular cross-section.
 6. The electrode as claimed in claim 1 in which the fibres have a substantially non-circular cross-section.
 7. A composite electrode containing bonded silicon-comprising fibres according to claim
 1. 8. A composite electrode as claimed in claim 7 which uses copper as a current collector.
 9. A composite electrode as claimed in claim 7 in which the electrode is an anode.
 10. An electrochemical cell containing a composite electrode as claimed in claim 7, wherein the composite electrode is an anode.
 11. The electrochemical cell as claimed in claim 10 further comprising a cathode in which the cathode comprises a lithium-containing compound capable of releasing and reabsorbing lithium ions as its active material.
 12. The electrochemical cell as claimed in claim 11 in which the cathode comprises lithium-based metal oxide, sulphide or phosphate as its active material.
 13. A lithium rechargeable cell anode comprising a layer of silicon-comprising fibres, wherein the silicon comprising fibres are arranged to cross over each other to provide multiple intersection points and characterized in that two or more of the fibres are bonded to each other at intersection points to form a bonded felt before any lithiation or delithiation of the silicon-comprising fibres, and wherein the fibres are single crystal fibres.
 14. An anode as claimed in claim 13 in which the fibres are the active components of a composite electrode.
 15. An anode as claimed in claim 13 including amorphous silicon portions at intersections of the fibres.
 16. A cell comprising an anode as claimed in claim 13 and a cathode.
 17. A cell as claimed in claim 16 in which the cathode comprises lithium-based material.
 18. A cell as claimed in claim 17 in which the cathode comprises lithium cobalt dioxide.
 19. A device powered by a cell as claimed in claim
 16. 20. An electrode for a lithium ion battery comprising an electrochemically active material comprising a layer of silicon-comprising fibres, wherein the silicon-comprising fibres are arranged to cross over each other to provide multiple intersection points, and characterized in that at least two of the silicon-comprising fibres are bonded to each other at intersection points to form a bonded felt before any lithiation or delithiation of the electrochemically active material.
 21. The electrode as claimed in claim 20 wherein a plurality of fibres are bonded together.
 22. The electrode as claimed in claim 20 in which the fibres have transverse dimensions in the range 0.08 to 0.5 microns and a length in the range 20 to 300 microns.
 23. The electrode as claimed in claim 20 in which the fibres have an aspect ratio of about 100:1.
 24. The electrode as claimed in claim 20 in which the fibres have a substantially circular cross-section.
 25. The electrode as claimed in claim 20 in which the fibres have a substantially non-circular cross-section.
 26. The electrode as claimed in claim 20 which uses copper as a current collector.
 27. The electrode as claimed in claim 20 in which the electrode is an anode.
 28. An electrochemical cell containing an electrode as claimed in claim
 27. 29. The electrochemical cell as claimed in claim 28 further comprising a cathode in which the cathode comprises a lithium-containing compound capable of releasing and reabsorbing lithium ions as its active material.
 30. The electrochemical cell as claimed in claim 29 in which the cathode comprises lithium-based metal oxide, sulphide or phosphate as its active material.
 31. The electrochemical cell as claimed in claim 30 in which the cathode comprises lithium cobalt dioxide.
 32. The electrode of claim 20 wherein at least one of the silicon comprising fibres is a single crystal fibre.
 33. The electrode of claim 20 including amorphous silicon portions at intersections of the fibres. 